PP fiber material is a kind of PP raw material for the base material added glass fiber processing of the profile, its mechanical properties and dimensional stability than the pure PP molding material is better, temperature resistance is also better. The operating temperature is -20-120°C
Characteristic：
1.Light weight, uniform thickness, smooth surface, good heat resistance, high mechanical strength, excellent chemical stability and electrical insulation,
2. Non-toxic, with excellent moisture absorption resistance, acid and alkali corrosion resistance, solubility resistance, high shrinkage rate.
| Shape | Colour | ||
 |  | ||
| Plate | Bar | Black | Natural Color |
| Thickness（mm） | Breadth（mm） | Length（mm） |
| 8-200 | 610/1000 | 1220/2000 |
| Diameter（mm） | Length（mm） |
| 8-200 | 1000 |
Specific gravit | ASTM D792 | g/cm3 | 1.13 |
Tensile yield strength | ASTM D638 | Mpa | 40 |
Breaking elongation | ASTM D638 | % | 20 |
Bending strength | ASTM D790 | Mpa | 54 |
Flexural modulus | ASTM D790 | Mpa | 3000 |
Shore hardness | ASTM D2240 | D | 85 |
Impact strength | ASTM D256 | J/M | 35 |
Melting point | DSC | °C | 190 |
Heat distortion temperature | ASTM D648 | °C | 95 |
Operating temperature | - | °C | 95 |
Maximum operating temperature | - | °C | 120 |
Coefficient of linear themal | ASTM D696 | 10-5-1/K | 19 |
Dielectric strength | ASTM D150 | KV-mm | 40 |
| Volume resistivit | ASTM D257 | Ω.cm | 1014 |
Surface resistivity | ASTM D257 | Ω | 1013 |
Dielectric constant | ASTM D149 | - | 2.3 |
Flammability | UL 94 | HB | |
Viscosity | - | + | |
Non toxic | EEC 90/128 FDA | + | |
Coefficient of friction | DIN 53375 | 0.3 | |
Anti-ultraviolet | - | 0 |
plate
Bar
Black
Green
Blue
Natural quality